Research subject: Poly (vinyl chloride) (PVC) is non-biodegradable, and the widespread use of conventional plasticizers, particularly phthalates, in its formulation poses significant risks to human health and the environment. In this research, various blends of PVC and poly (lactic acid) (PLA) with different ratios were prepared in an internal mixer. The effect of PLA content, as well as the influence of various plasticizers including dioctyl phthalate (DOP), dioctyl adipate (DOA), epoxidized soybean oil (ESO), and chlorinated paraffin wax, on the mechanical and biodegradability properties was investigated. Furthermore, the role of a compatibilizer in improving the distribution of the PLA phase and increasing the compatibility between the polymers was evaluated.
Research approach: Tensile testing and dynamic mechanical analysis (DMTA) were performed to study the mechanical behavior. Scanning electron microscopy (SEM) imaging was used to examine the morphology and the distribution of the PLA phase. In addition, a biodegradability test was carried out to analyze the degradation behavior of samples in the environment.
Main results: The results indicated that the PVC/PLA(90/10)-DOP blend exhibited a suitable distribution of the PLA phase within the PVC matrix, whereas a poor distribution of PLA in PVC was observed in the PVC/PLA(80/20)-DOP blend. The addition of a compatibilizer to the PVC/PLA(80/20)-DOP sample led to increased uniformity in the PLA phase distribution and improved tensile strength. Samples with higher PLA content showed greater biodegradability behavior, suggesting the role of PLA as a degradability-enhancing agent. The comparison of different plasticizers indicated that several of the ones used in this research exhibit properties comparable to DOP and may be considered as effective substitutes for it. The findings suggest that the simultaneous use of PLA and appropriate plasticizers such as ESO, along with the application of a compatibilizer, is an effective method for producing PVC samples with enhanced mechanical and biodegradability properties.